Toward a design for flowable and extensible ionomers: An example of diamine-neutralized entangled poly(styrene-co-4-vinylbenzoic acid) ionomer melts
Publikation: Bidrag til tidsskrift › Tidsskriftartikel › Forskning › fagfællebedømt
Standard
Toward a design for flowable and extensible ionomers : An example of diamine-neutralized entangled poly(styrene-co-4-vinylbenzoic acid) ionomer melts. / Skov, Anne L.; Huang, Qian; Wang, Wendi; Madsen, Jeppe; Genina, Natalja; Hassager, Ole.
I: Macromolecules, Bind 54, Nr. 5, 2021, s. 2306-2315.Publikation: Bidrag til tidsskrift › Tidsskriftartikel › Forskning › fagfællebedømt
Harvard
APA
Vancouver
Author
Bibtex
}
RIS
TY - JOUR
T1 - Toward a design for flowable and extensible ionomers
T2 - An example of diamine-neutralized entangled poly(styrene-co-4-vinylbenzoic acid) ionomer melts
AU - Skov, Anne L.
AU - Huang, Qian
AU - Wang, Wendi
AU - Madsen, Jeppe
AU - Genina, Natalja
AU - Hassager, Ole
PY - 2021
Y1 - 2021
N2 - Processing ionomers is complicated by their ability to exhibit brittle fracture even in the melt state. This work introduces a new strategy for providing ionomers with good flowability, extensibility, and superior strain hardening. Diamineneutralized entangled poly(styrene-co-4-vinylbenzoic acid) ionomers were studied using small-amplitude oscillatory shear and nonlinear uniaxial extension measurements. The parent molecule, poly(styrene-co-4-vinylbenzoic acid), has a molar mass of 85,400 g/mol, well above the entanglement molar mass of polystyrene (13,300 g/mol). Neutralization was performed using "Jeffamine" type diamines with different molar masses. The resulting neutralized ionomers presented relaxation processes similar to entangled polymers but with faster terminal relaxation, suggesting negligible ionic cluster formation and indicating a diluting effect of the introduced diamines. This feature provides the ionomers with good flowability and facilitates their processing. In extensional measurements, these ionomers displayed superior strain hardening compared to the parent molecule, which also proved to be adjustable via changing diamine length. The stress growth curves showed a maximum stress, followed by stress overshoot and steady state at larger strain. The stress maximum and overshoot were correlated with ionic sticker disassociation, as evidenced by phase separation-induced color change during filament stretching. At high stretch rates, the stickers disassociate abruptly to accommodate the strain, so that the sticker disassociation time decreased with increasing stretch rates. Good extensibility (up to Hencky strain 7) was achieved via ionic sticker reassociation and entanglements.
AB - Processing ionomers is complicated by their ability to exhibit brittle fracture even in the melt state. This work introduces a new strategy for providing ionomers with good flowability, extensibility, and superior strain hardening. Diamineneutralized entangled poly(styrene-co-4-vinylbenzoic acid) ionomers were studied using small-amplitude oscillatory shear and nonlinear uniaxial extension measurements. The parent molecule, poly(styrene-co-4-vinylbenzoic acid), has a molar mass of 85,400 g/mol, well above the entanglement molar mass of polystyrene (13,300 g/mol). Neutralization was performed using "Jeffamine" type diamines with different molar masses. The resulting neutralized ionomers presented relaxation processes similar to entangled polymers but with faster terminal relaxation, suggesting negligible ionic cluster formation and indicating a diluting effect of the introduced diamines. This feature provides the ionomers with good flowability and facilitates their processing. In extensional measurements, these ionomers displayed superior strain hardening compared to the parent molecule, which also proved to be adjustable via changing diamine length. The stress growth curves showed a maximum stress, followed by stress overshoot and steady state at larger strain. The stress maximum and overshoot were correlated with ionic sticker disassociation, as evidenced by phase separation-induced color change during filament stretching. At high stretch rates, the stickers disassociate abruptly to accommodate the strain, so that the sticker disassociation time decreased with increasing stretch rates. Good extensibility (up to Hencky strain 7) was achieved via ionic sticker reassociation and entanglements.
U2 - 10.1021/acs.macromol.0c02408
DO - 10.1021/acs.macromol.0c02408